Details

The presence of sulfuric compounds in the air causes silver and silver coatings to develop tarnish on their surfaces, which is a significant issue. To address this problem, transparent ceramic coatings were created through physical vapor deposition (PVD) to act as tarnish barriers. The AlN and Al₂O₃ films, known for their transparency in the visible spectrum, chemical stability, and high oxidation resistance, are particularly intriguing. In this study, Ag sheets with purities of 99.9% and 92.5% were coated with multilayer AlN/Al₂O₃ film using the PVD technique. The microstructure and composition of the coatings were analyzed using X-ray photoelectron spectroscopy (XPS). The color of the multilayer AlN/Al₂O₃ film was assessed using the Commission Internationale de l'Eclairage (CIE) method. The tarnish resistance of the coatings was tested by exposing them to a sulfur atmosphere in a specialized setup. A comparison with uncoated Ag sheets revealed that the results of the multilayer AlN/Al₂O₃ film coatings were excellent. Thus, the application of the multilayer AlN/Al₂O₃ film coating proves to be a suitable method for protecting silver jewelry from tarnish.

Objective

เนื่องจากเครื่องประดับเงินมีความนิยมอย่างแพร่หลายในอุตสาหกรรมเครื่องประดับแต่เมื่อใช้งานเป็นระยะเวลานานส่งผลให้เกิดการหมองบนเครื่องประดับเงิน โดยการทำโครงงานการป้องกันการหมองเครื่องประดับเงินด้วยการเคลือบฟิล์มอะลูมิเนียมไนไตรด์และฟิล์มอะลูมิเนียมออกไซด์หลายชั้น สามารถทำให้เครื่องประดับเงินสามารถคงความสวยงามไม่เกิดการหมองได้ จึงได้สนใจในการทำโครงงานนี้

Project Members

ชยานันต์ ภวินท์พร

CHAYANUN PAVINPORN

#นักศึกษา

Member

ศุภกร ไชยศล

SUPHAKORN CHAISOL

#นักศึกษา

Member

อาภาภรณ์ สกุลการะเวก

Aparporn Sakulkalavek

#อาจารย์

Advisor

Vote for this Innovation!